Phenolic resin was modified respectively using four latexes of butyronitrile-butadiene,carboxylic butyronitrile-butadiene,styrene-butadiene and pyridine-butadiene.

采用丁腈、羧基丁腈、丁苯、丁吡四种胶乳改性酚树脂。

This paper summarizes the preparation method, performance, progress of application and direction of studying phenolic resin acticarbon.

概述了酚树脂基活性炭的制备方法、性能及其应用展和主要研究方向。

The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.

本文研究了用酚化木材制备酚树脂的技术,并对其性能行分析。

The presence of inauthentic Bakelite out there led to an early 20th century version of the "Intel In-side" logo.

从那儿开始的假冒酚塑料的出现引出了20世纪早期的“IntelInside”商标形式。

Benzylic ether phenolic resin is one of the main components of foundry polyurethane binder; its structure and preparation condition determine the performances of polyurethane binder.

苯醚型酚树脂是铸造用聚氨酯粘合剂的主要成份之一,它的结构及合成工艺条件决定了该类粘合剂性能。

A foamable phenolic resin was prepared,through addition,condensation,in the presence of alkali.The resin was foamed with surfactant, foamer,solidifying agent , then the foam phenolplast was given .

苯酚与甲性条件下经加成、缩合制得可发性酚树脂，该树脂和表面活性剂、发泡剂、固化剂一起发泡即得酚泡沫塑料。

It was shown that the curing process of resoles, at first, proceeded by condensation reaction of methylol groups, and the formation of dimethylene ether linkage was predominant.

结果表明热固性酚树脂的固化过程,首先是羟甲基发生缩合反应,缩合反应形成醚键是主要的。

Phenolic resin was modified respectively using four latexes of butyronitrile-butadiene,carboxylic butyronitrile-butadiene,styrene-butadiene and pyridine-butadiene.

采丁腈、羧基丁腈、丁苯、丁吡四种胶乳改性酚醛树脂。

This paper summarizes the preparation method, performance, progress of application and direction of studying phenolic resin acticarbon.

概述了酚醛树脂基活性炭的法、性能及其应展和主要研究向。

The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.

本文研究了酚化木材酚醛树脂的技术,并对其性能行分析。

The presence of inauthentic Bakelite out there led to an early 20th century version of the "Intel In-side" logo.

从那儿开始的假冒酚醛塑料的出现引出了20世纪早期的“IntelInside”商标形式。

Benzylic ether phenolic resin is one of the main components of foundry polyurethane binder; its structure and preparation condition determine the performances of polyurethane binder.

苯醚型酚醛树脂是铸造酯粘合剂的主要成份之一,它的结构及合成工艺条件决定了该类粘合剂性能。

A foamable phenolic resin was prepared,through addition,condensation,in the presence of alkali.The resin was foamed with surfactant, foamer,solidifying agent , then the foam phenolplast was given .

苯酚与甲醛在碱性条件下经加成、缩合得可发性酚醛树脂，该树脂和表面活性剂、发泡剂、固化剂一起发泡即得酚醛泡沫塑料。

It was shown that the curing process of resoles, at first, proceeded by condensation reaction of methylol groups, and the formation of dimethylene ether linkage was predominant.

结果表明热固性酚醛树脂的固化过程,首先是羟甲基发生缩合反应,缩合反应形成醚键是主要的。

Phenolic resin was modified respectively using four latexes of butyronitrile-butadiene,carboxylic butyronitrile-butadiene,styrene-butadiene and pyridine-butadiene.

采用丁腈、羧基丁腈、丁苯、丁吡四种胶乳改性酚醛树脂。

This paper summarizes the preparation method, performance, progress of application and direction of studying phenolic resin acticarbon.

概述酚醛树脂基活性炭的制备方法、性能及其应用展和主要方向。

The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.

本文用酚化木材制备酚醛树脂的技术,并对其性能行分析。

The presence of inauthentic Bakelite out there led to an early 20th century version of the "Intel In-side" logo.

从那儿开始的假冒酚醛塑料的现引20纪早期的“IntelInside”商标形式。

Benzylic ether phenolic resin is one of the main components of foundry polyurethane binder; its structure and preparation condition determine the performances of polyurethane binder.

苯醚型酚醛树脂是铸造用聚氨酯粘合剂的主要成份之一,它的结构及合成工艺条件决定该类粘合剂性能。

A foamable phenolic resin was prepared,through addition,condensation,in the presence of alkali.The resin was foamed with surfactant, foamer,solidifying agent , then the foam phenolplast was given .

苯酚与甲醛在碱性条件下经加成、缩合制得可发性酚醛树脂，该树脂和表面活性剂、发泡剂、固化剂一起发泡即得酚醛泡沫塑料。

It was shown that the curing process of resoles, at first, proceeded by condensation reaction of methylol groups, and the formation of dimethylene ether linkage was predominant.

结果表明热固性酚醛树脂的固化过程,首先是羟甲基发生缩合反应,缩合反应形成醚键是主要的。

Phenolic resin was modified respectively using four latexes of butyronitrile-butadiene,carboxylic butyronitrile-butadiene,styrene-butadiene and pyridine-butadiene.

采用丁腈、羧基丁腈、丁、丁吡四种胶乳改性酚醛树脂。

This paper summarizes the preparation method, performance, progress of application and direction of studying phenolic resin acticarbon.

概述了酚醛树脂基活性炭的制备方法、性能及其应用要研究方向。

The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.

本文研究了用酚化木材制备酚醛树脂的技术,并对其性能行分析。

The presence of inauthentic Bakelite out there led to an early 20th century version of the "Intel In-side" logo.

从那儿开始的假冒酚醛塑料的出现引出了20世纪早期的“IntelInside”商标形。

Benzylic ether phenolic resin is one of the main components of foundry polyurethane binder; its structure and preparation condition determine the performances of polyurethane binder.

型酚醛树脂是铸造用聚氨酯粘合剂的要成份之一,它的结构及合成工艺条件决定了该类粘合剂性能。

A foamable phenolic resin was prepared,through addition,condensation,in the presence of alkali.The resin was foamed with surfactant, foamer,solidifying agent , then the foam phenolplast was given .

酚与甲醛在碱性条件下经加成、缩合制得可发性酚醛树脂，该树脂表面活性剂、发泡剂、固化剂一起发泡即得酚醛泡沫塑料。

It was shown that the curing process of resoles, at first, proceeded by condensation reaction of methylol groups, and the formation of dimethylene ether linkage was predominant.

结果表明热固性酚醛树脂的固化过程,首先是羟甲基发生缩合反应,缩合反应形成键是要的。

Phenolic resin was modified respectively using four latexes of butyronitrile-butadiene,carboxylic butyronitrile-butadiene,styrene-butadiene and pyridine-butadiene.

采丁腈、羧基丁腈、丁苯、丁吡四种胶乳改性醛树脂。

This paper summarizes the preparation method, performance, progress of application and direction of studying phenolic resin acticarbon.

概述了醛树脂基活性炭的制备方法、性能及其应和主要研究方向。

The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.

本文研究了化木材制备醛树脂的技术,并对其性能行分析。

The presence of inauthentic Bakelite out there led to an early 20th century version of the "Intel In-side" logo.

从那儿开始的假冒醛塑料的出现引出了20世纪早期的“IntelInside”商标形式。

Benzylic ether phenolic resin is one of the main components of foundry polyurethane binder; its structure and preparation condition determine the performances of polyurethane binder.

苯醛树脂是铸造聚氨酯粘合剂的主要成份之一,它的结构及合成工艺条件决定了该类粘合剂性能。

A foamable phenolic resin was prepared,through addition,condensation,in the presence of alkali.The resin was foamed with surfactant, foamer,solidifying agent , then the foam phenolplast was given .

苯与甲醛在碱性条件下经加成、缩合制得可发性醛树脂，该树脂和表面活性剂、发泡剂、固化剂一起发泡即得醛泡沫塑料。

It was shown that the curing process of resoles, at first, proceeded by condensation reaction of methylol groups, and the formation of dimethylene ether linkage was predominant.

结果表明热固性醛树脂的固化过程,首先是羟甲基发生缩合反应,缩合反应形成键是主要的。

Phenolic resin was modified respectively using four latexes of butyronitrile-butadiene,carboxylic butyronitrile-butadiene,styrene-butadiene and pyridine-butadiene.

采用丁腈、羧基丁腈、丁苯、丁吡四种胶乳改性酚醛树脂。

This paper summarizes the preparation method, performance, progress of application and direction of studying phenolic resin acticarbon.

概述了酚醛树脂基活性炭的制备方法、性能及应用展和主要研究方向。

The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.

本文研究了用酚化木材制备酚醛树脂的技术,性能行分。

The presence of inauthentic Bakelite out there led to an early 20th century version of the "Intel In-side" logo.

儿开始的假冒酚醛塑料的出现引出了20世纪早期的“IntelInside”商标形式。

Benzylic ether phenolic resin is one of the main components of foundry polyurethane binder; its structure and preparation condition determine the performances of polyurethane binder.

苯醚型酚醛树脂是铸造用聚氨酯粘合剂的主要成份之一,它的结构及合成工艺条件决定了该类粘合剂性能。

A foamable phenolic resin was prepared,through addition,condensation,in the presence of alkali.The resin was foamed with surfactant, foamer,solidifying agent , then the foam phenolplast was given .

苯酚与甲醛在碱性条件下经加成、缩合制得可发性酚醛树脂，该树脂和表面活性剂、发泡剂、固化剂一起发泡即得酚醛泡沫塑料。

It was shown that the curing process of resoles, at first, proceeded by condensation reaction of methylol groups, and the formation of dimethylene ether linkage was predominant.

结果表明热固性酚醛树脂的固化过程,首先是羟甲基发生缩合反应,缩合反应形成醚键是主要的。

Phenolic resin was modified respectively using four latexes of butyronitrile-butadiene,carboxylic butyronitrile-butadiene,styrene-butadiene and pyridine-butadiene.

采用丁腈、羧基丁腈、丁苯、丁吡四种胶乳改性脂。

This paper summarizes the preparation method, performance, progress of application and direction of studying phenolic resin acticarbon.

概述了脂基活性炭的制备方法、性能其应用展和主要研究方向。

The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.

本文研究了用化木材制备脂的技术,并对其性能行分析。

The presence of inauthentic Bakelite out there led to an early 20th century version of the "Intel In-side" logo.

从那儿开始的假冒塑料的出现引出了20世纪早期的“IntelInside”商标形式。

Benzylic ether phenolic resin is one of the main components of foundry polyurethane binder; its structure and preparation condition determine the performances of polyurethane binder.

苯醚型脂是铸造用聚氨酯粘合剂的主要成份之一,它的合成工艺条件决定了该类粘合剂性能。

A foamable phenolic resin was prepared,through addition,condensation,in the presence of alkali.The resin was foamed with surfactant, foamer,solidifying agent , then the foam phenolplast was given .

苯与甲在碱性条件下经加成、缩合制得可发性脂，该脂和表面活性剂、发泡剂、固化剂一起发泡即得泡沫塑料。

It was shown that the curing process of resoles, at first, proceeded by condensation reaction of methylol groups, and the formation of dimethylene ether linkage was predominant.

果表明热固性脂的固化过程,首先是羟甲基发生缩合反应,缩合反应形成醚键是主要的。

Phenolic resin was modified respectively using four latexes of butyronitrile-butadiene,carboxylic butyronitrile-butadiene,styrene-butadiene and pyridine-butadiene.

采用丁腈、羧基丁腈、丁苯、丁吡四种胶乳改性酚树脂。

This paper summarizes the preparation method, performance, progress of application and direction of studying phenolic resin acticarbon.

概述了酚树脂基活性炭的制备方法、性能及其应用展和主要研究方向。

The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.

本文研究了用酚化木材制备酚树脂的技术,并对其性能行分析。

The presence of inauthentic Bakelite out there led to an early 20th century version of the "Intel In-side" logo.

从那儿开始的假冒酚塑料的出现引出了20世纪早期的“IntelInside”商标形式。

Benzylic ether phenolic resin is one of the main components of foundry polyurethane binder; its structure and preparation condition determine the performances of polyurethane binder.

苯醚型酚树脂是铸造用聚氨酯粘合剂的主要成份之一,它的结构及合成工艺条件决定了该类粘合剂性能。

A foamable phenolic resin was prepared,through addition,condensation,in the presence of alkali.The resin was foamed with surfactant, foamer,solidifying agent , then the foam phenolplast was given .

苯酚在碱性条件下经加成、缩合制得可发性酚树脂，该树脂和表面活性剂、发泡剂、固化剂一起发泡即得酚泡沫塑料。

It was shown that the curing process of resoles, at first, proceeded by condensation reaction of methylol groups, and the formation of dimethylene ether linkage was predominant.

结果表明热固性酚树脂的固化过程,首先是羟基发生缩合反应,缩合反应形成醚键是主要的。

Phenolic resin was modified respectively using four latexes of butyronitrile-butadiene,carboxylic butyronitrile-butadiene,styrene-butadiene and pyridine-butadiene.

采用丁腈、羧基丁腈、丁苯、丁吡四种胶乳改性树脂。

This paper summarizes the preparation method, performance, progress of application and direction of studying phenolic resin acticarbon.

概述树脂基活性炭的制备方法、性能及其应用展和主要研究方向。

The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.

本文研究用化木材制备树脂的技术,并对其性能行分析。

The presence of inauthentic Bakelite out there led to an early 20th century version of the "Intel In-side" logo.

从那儿开始的假冒塑料的出现引出20世纪早期的“IntelInside”商标形式。

Benzylic ether phenolic resin is one of the main components of foundry polyurethane binder; its structure and preparation condition determine the performances of polyurethane binder.

苯醚型树脂是铸造用聚氨酯粘合剂的主要一,它的结构及合工艺条件决定该类粘合剂性能。

A foamable phenolic resin was prepared,through addition,condensation,in the presence of alkali.The resin was foamed with surfactant, foamer,solidifying agent , then the foam phenolplast was given .

苯与甲在碱性条件下经加、缩合制得可发性树脂，该树脂和表面活性剂、发泡剂、固化剂一起发泡即得泡沫塑料。

It was shown that the curing process of resoles, at first, proceeded by condensation reaction of methylol groups, and the formation of dimethylene ether linkage was predominant.

结果表明热固性树脂的固化过程,首先是羟甲基发生缩合反应,缩合反应形醚键是主要的。