A test of arrosion performance of anticorrocive built-up weld layer in different meeiums was con-ducted by using a self-made arrosion testing machine.

用自制腐蚀损试验机对耐蚀堆焊在不同介质中腐蚀损性能进行试验，结果表明：腐蚀介质不同，堆焊损速率也不同。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形析、光学金相、扫描电镜能谱析等测试方法，双药皮对钛钙型不锈钢焊条气孔影响。

The contact between welding plate and fixture is treated as constraint in the finite element model of dynamic welding angular distortion simulation for overlayer in CO2 gas arc welding.

摘要采用有限元数值模拟方法CO2气体保护堆焊角变形动态过程。为反映夹具和焊接件接触状态，将夹具和焊件统一建立有限元模型。

A test of arrosion performance of anticorrocive built-up weld layer in different meeiums was con-ducted by using a self-made arrosion testing machine.

用自制的腐蚀磨损试验机对耐蚀堆焊层在不中的腐蚀磨损性能进行了试验，结果表明：腐蚀不，堆焊层的磨损速率也不。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形析、光学金相、扫描电镜能谱析等测试方法，研究了双层药皮对钛钙型不锈钢焊条气孔的影响。

The contact between welding plate and fixture is treated as constraint in the finite element model of dynamic welding angular distortion simulation for overlayer in CO2 gas arc welding.

摘要采用有限元拟方法研究了CO2气体保护堆焊的角变形动态过程。为了反映夹具和焊接件的接触状态，将夹具和焊件统一建立有限元型。

A test of arrosion performance of anticorrocive built-up weld layer in different meeiums was con-ducted by using a self-made arrosion testing machine.

用自制的腐蚀磨机对耐蚀层在不同介质中的腐蚀磨性能进行了，结果表明：腐蚀介质不同，层的磨速率也不同。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板、高速摄影、波形析、光学金相、扫描电镜能谱析等测方法，研究了双层药皮对钛钙型不锈钢条气孔的影响。

The contact between welding plate and fixture is treated as constraint in the finite element model of dynamic welding angular distortion simulation for overlayer in CO2 gas arc welding.

摘要采用有限元数值模拟方法研究了CO2气体保的角变形动态过程。为了反映夹具和接件的接触状态，将夹具和件统一建立有限元模型。

A test of arrosion performance of anticorrocive built-up weld layer in different meeiums was con-ducted by using a self-made arrosion testing machine.

用自制的腐蚀磨损试验机对耐蚀堆焊层在不同介质中的腐蚀磨损性能进行试验，结果表明：腐蚀介质不同，堆焊层的磨损速率也不同。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形析、光学金相、扫描电镜能谱析等测试方法，研究双层药皮对钛钙型不锈钢焊条气孔的影响。

The contact between welding plate and fixture is treated as constraint in the finite element model of dynamic welding angular distortion simulation for overlayer in CO2 gas arc welding.

摘要采用有限元数值模拟方法研究CO2气体保护堆焊的角变形动态过。反映夹具和焊接件的接触状态，将夹具和焊件统一建立有限元模型。

A test of arrosion performance of anticorrocive built-up weld layer in different meeiums was con-ducted by using a self-made arrosion testing machine.

用自制的腐蚀磨验机对耐蚀堆焊层在不同介质中的腐蚀磨性能进行了验，结果表明：腐蚀介质不同，堆焊层的磨也不同。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高摄影、波形析、光学金相、扫描电镜能谱析等测法，研究了双层药皮对钛钙型不锈钢焊条气孔的影响。

The contact between welding plate and fixture is treated as constraint in the finite element model of dynamic welding angular distortion simulation for overlayer in CO2 gas arc welding.

摘要采用有限元数值模拟法研究了CO2气体保护堆焊的角变形动态过程。为了反映夹具和焊接件的接触状态，将夹具和焊件统一建立有限元模型。

A test of arrosion performance of anticorrocive built-up weld layer in different meeiums was con-ducted by using a self-made arrosion testing machine.

用自制的腐蚀磨损试验机对耐蚀堆焊层在不同介质中的腐蚀磨损性能进行试验，结果表明：腐蚀介质不同，堆焊层的磨损速率也不同。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形析、光学金相、扫描电镜能谱析等测试方法，研究双层药皮对钛钙型不锈钢焊条气孔的影响。

The contact between welding plate and fixture is treated as constraint in the finite element model of dynamic welding angular distortion simulation for overlayer in CO2 gas arc welding.

摘要采用有限元数值模拟方法研究CO2气体保护堆焊的角变形动态过。反映夹具和焊接件的接触状态，将夹具和焊件统一建立有限元模型。

A test of arrosion performance of anticorrocive built-up weld layer in different meeiums was con-ducted by using a self-made arrosion testing machine.

用自制的腐蚀磨损试验机对耐蚀堆焊层在质中的腐蚀磨损性能进行了试验，结果表明：腐蚀质，堆焊层的磨损速率也。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形析、光学金相、扫描电镜能谱析等测试方法，研究了双层药皮对钛钙型锈钢焊条气孔的影响。

The contact between welding plate and fixture is treated as constraint in the finite element model of dynamic welding angular distortion simulation for overlayer in CO2 gas arc welding.

摘要采用有限元数方法研究了CO2气体保护堆焊的角变形动态过程。为了反映夹具和焊接件的接触状态，将夹具和焊件统一建立有限元型。

A test of arrosion performance of anticorrocive built-up weld layer in different meeiums was con-ducted by using a self-made arrosion testing machine.

用自制的腐蚀磨损试验机对耐蚀堆焊层在不同介质中的腐蚀磨损性能进行了试验，结果表明：腐蚀介质不同，堆焊层的磨损速率也不同。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形析、光学金相、扫描电镜能谱析等测试方法，研究了双层药皮对钛钙型不锈钢焊条气孔的影响。

The contact between welding plate and fixture is treated as constraint in the finite element model of dynamic welding angular distortion simulation for overlayer in CO2 gas arc welding.

摘要采用有限元数值模拟方法研究了CO2气体保护堆焊的角变形动态过程。为了具和焊接件的接触状态，将具和焊件统一建立有限元模型。

A test of arrosion performance of anticorrocive built-up weld layer in different meeiums was con-ducted by using a self-made arrosion testing machine.

用自制的腐蚀磨损试验机对耐蚀堆焊层在不同的腐蚀磨损性能进行了试验，结果表明：腐蚀不同，堆焊层的磨损速率也不同。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形析、光学金相、扫描电镜能谱析等测试方法，研究了双层药皮对钛钙型不锈钢焊条气孔的影响。

The contact between welding plate and fixture is treated as constraint in the finite element model of dynamic welding angular distortion simulation for overlayer in CO2 gas arc welding.

摘要采用有限模拟方法研究了CO2气体保护堆焊的角变形动态过程。为了反映夹具和焊接件的接触状态，将夹具和焊件统一建立有限模型。