The reaction between polystyrene having oxazoline groups(RPS) and chlorinated polyethylene(CPE) was investigated by FTIR, DSC methods.

用FTIR、DSC等法究了含恶唑啉官能团的聚苯乙烯(RPS)与氯化聚乙烯(CPE)之间的反应。

The thermal decomposition of single, double-and triple-base nitroguanidine propellants was studied by differential scanning calorimetry (DSC).

用差示扫描量热计（DSC）究了单基、双基三基药热分解性能。

The structure and properties of polyorganosiloxane-acrylate emulsion copolymer were investigated by IR, XPS, DSC, 1H-NMR, WAXD.

利用红外光谱、光电子能谱、差热分析、核磁共振、X射线衍射等法对聚硅氧改性丙烯酸酯共聚物的结构性能进行了究。

The dehydriding temperature and dehydriding capacity were evaluated by differential scanning calorimeter (DSC) and thermogravimetric analysis (TG).

运用差热分析热重分析对储氢材料的放氢温度放氢量进行了测试。

The crystallization porperty of polycaprolactam(PA6)-polyethylene glycol(PEG)block copolymer wasinvestigated by means of electron microscope,x-ray diffraction,DSC and hot stage polarized microscope.

应用DSC、热台、扫描电镜以及偏光显微镜等究了PA6-PEG嵌段共聚物的结晶性能。

The effect of ethylene comonomer content on the crystallization, mechanical and viscoelastic properties of VERSIFY copolymers was studied by DSC, DMTA, POM and WAXD.

DSC，DMTA，POMWAXD等手段，究了乙烯共聚单体含量的变化对VERSIFY共聚物结晶性能、力学性能粘弹性能的影响。

During heating,phase transformation and expansibility of the new quartz sands and the calcined Quartz sands from two places were determined by DSC and thermodilatometry.

本究采用DSC热膨胀仪对两种石英砂的原砂焙烧砂在加热程中的相变热膨胀进行了分析。

The changing of the structure and properties of UHMWPE fibres during super drawing were studied by means of SEM, DSC, WAXD and sound pulsimeter.

还借助扫描电子显微镜（SEM）、热分析（DSC）、广角X射线衍射（WAXD）、声速等手段究了UHMWPE熔纺丝在超拉伸程中结构性能的变化。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

The photographs of polarizing microscope showed the number of spherocrystal was increased and the diameter was decreased after saponification reaction which was agreed with the studies of DSC.

试样的偏光显微镜观察结果表明，醇解后，球晶数目增加、直径减小、完善程度降低。

The reaction between polystyrene having oxazoline groups(RPS) and chlorinated polyethylene(CPE) was investigated by FTIR, DSC methods.

用FTIR、DSC等方法研究了含恶唑啉官能团的苯乙(RPS)与氯化乙(CPE)之间的反应。

The thermal decomposition of single, double-and triple-base nitroguanidine propellants was studied by differential scanning calorimetry (DSC).

用差示扫描量热计（DSC）研究了单基、双基和三基药热分解性能。

The structure and properties of polyorganosiloxane-acrylate emulsion copolymer were investigated by IR, XPS, DSC, 1H-NMR, WAXD.

利用红外光谱、光电子能谱、差热分析、核磁振、X射线衍射等方法对硅氧改性丙酸酯物的结构和性能进行了研究。

The dehydriding temperature and dehydriding capacity were evaluated by differential scanning calorimeter (DSC) and thermogravimetric analysis (TG).

运用差热分析和热重分析对储氢材料的放氢温度和放氢量进行了测试。

The crystallization porperty of polycaprolactam(PA6)-polyethylene glycol(PEG)block copolymer wasinvestigated by means of electron microscope,x-ray diffraction,DSC and hot stage polarized microscope.

应用DSC、热台、扫描电镜以及偏光显微镜等研究了PA6-PEG嵌段物的结晶性能。

The effect of ethylene comonomer content on the crystallization, mechanical and viscoelastic properties of VERSIFY copolymers was studied by DSC, DMTA, POM and WAXD.

通过DSC，DMTA，POM和WAXD等手段，研究了乙单体含量的变化对VERSIFY物结晶性能、力性能和粘弹性能的影响。

During heating,phase transformation and expansibility of the new quartz sands and the calcined Quartz sands from two places were determined by DSC and thermodilatometry.

本研究采用DSC和热膨胀仪对两种石英砂的原砂和焙烧砂在加热过程中的相变和热膨胀进行了分析。

The changing of the structure and properties of UHMWPE fibres during super drawing were studied by means of SEM, DSC, WAXD and sound pulsimeter.

还借助扫描电子显微镜（SEM）、热分析（DSC）、广角X射线衍射（WAXD）、声速等手段研究了UHMWPE熔纺丝在超拉伸过程中结构性能的变化。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

The photographs of polarizing microscope showed the number of spherocrystal was increased and the diameter was decreased after saponification reaction which was agreed with the studies of DSC.

试样的偏光显微镜观察结果表明，醇解后，球晶数目增加、直径减小、完善程度降低。

The reaction between polystyrene having oxazoline groups(RPS) and chlorinated polyethylene(CPE) was investigated by FTIR, DSC methods.

用FTIR、DSC等方法研究含恶唑啉官能团的聚苯乙烯(RPS)与氯化聚乙烯(CPE)之间的反应。

The thermal decomposition of single, double-and triple-base nitroguanidine propellants was studied by differential scanning calorimetry (DSC).

用差示扫计（DSC）研究单基、双基和三基药分解性能。

The structure and properties of polyorganosiloxane-acrylate emulsion copolymer were investigated by IR, XPS, DSC, 1H-NMR, WAXD.

利用红外光谱、光电子能谱、差分析、核磁共振、X射线衍射等方法对聚硅氧改性丙烯酸酯共聚物的结构和性能进行研究。

The dehydriding temperature and dehydriding capacity were evaluated by differential scanning calorimeter (DSC) and thermogravimetric analysis (TG).

运用差分析和重分析对储氢材料的放氢温度和放氢进行。

The crystallization porperty of polycaprolactam(PA6)-polyethylene glycol(PEG)block copolymer wasinvestigated by means of electron microscope,x-ray diffraction,DSC and hot stage polarized microscope.

应用DSC、台、扫电镜以及偏光显微镜等研究PA6-PEG嵌段共聚物的结晶性能。

The effect of ethylene comonomer content on the crystallization, mechanical and viscoelastic properties of VERSIFY copolymers was studied by DSC, DMTA, POM and WAXD.

通过DSC，DMTA，POM和WAXD等手段，研究乙烯共聚单体含的变化对VERSIFY共聚物结晶性能、力学性能和粘弹性能的影响。

During heating,phase transformation and expansibility of the new quartz sands and the calcined Quartz sands from two places were determined by DSC and thermodilatometry.

本研究采用DSC和膨胀仪对两种石英砂的原砂和焙烧砂在加过程中的相变和膨胀进行分析。

The changing of the structure and properties of UHMWPE fibres during super drawing were studied by means of SEM, DSC, WAXD and sound pulsimeter.

还借助扫电子显微镜（SEM）、分析（DSC）、广角X射线衍射（WAXD）、声速等手段研究UHMWPE熔纺丝在超拉伸过程中结构性能的变化。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

The photographs of polarizing microscope showed the number of spherocrystal was increased and the diameter was decreased after saponification reaction which was agreed with the studies of DSC.

样的偏光显微镜观察结果表明，醇解后，球晶数目增加、直径减小、完善程度降低。

The reaction between polystyrene having oxazoline groups(RPS) and chlorinated polyethylene(CPE) was investigated by FTIR, DSC methods.

用FTIR、DSC方法研究了含恶唑啉官能团的聚苯乙(RPS)化聚乙(CPE)之间的反应。

The thermal decomposition of single, double-and triple-base nitroguanidine propellants was studied by differential scanning calorimetry (DSC).

用差示扫描量热计（DSC）研究了单基、双基和三基药热分解性能。

The structure and properties of polyorganosiloxane-acrylate emulsion copolymer were investigated by IR, XPS, DSC, 1H-NMR, WAXD.

利用红外光谱、光电子能谱、差热分析、核磁共振、X射线衍射方法对聚硅氧改性丙酸酯共聚物的结构和性能进行了研究。

The dehydriding temperature and dehydriding capacity were evaluated by differential scanning calorimeter (DSC) and thermogravimetric analysis (TG).

运用差热分析和热重分析对储氢材料的放氢温度和放氢量进行了测试。

The crystallization porperty of polycaprolactam(PA6)-polyethylene glycol(PEG)block copolymer wasinvestigated by means of electron microscope,x-ray diffraction,DSC and hot stage polarized microscope.

应用DSC、热台、扫描电以及偏光显研究了PA6-PEG嵌段共聚物的结晶性能。

The effect of ethylene comonomer content on the crystallization, mechanical and viscoelastic properties of VERSIFY copolymers was studied by DSC, DMTA, POM and WAXD.

通过DSC，DMTA，POM和WAXD手段，研究了乙共聚单体含量的变化对VERSIFY共聚物结晶性能、力学性能和粘弹性能的影响。

During heating,phase transformation and expansibility of the new quartz sands and the calcined Quartz sands from two places were determined by DSC and thermodilatometry.

本研究采用DSC和热膨胀仪对两种石英砂的原砂和焙烧砂在加热过程中的相变和热膨胀进行了分析。

The changing of the structure and properties of UHMWPE fibres during super drawing were studied by means of SEM, DSC, WAXD and sound pulsimeter.

还借助扫描电子显（SEM）、热分析（DSC）、广角X射线衍射（WAXD）、声速手段研究了UHMWPE熔纺丝在超拉伸过程中结构性能的变化。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

The photographs of polarizing microscope showed the number of spherocrystal was increased and the diameter was decreased after saponification reaction which was agreed with the studies of DSC.

试样的偏光显观察结果表明，醇解后，球晶数目增加、直径减小、完善程度降低。

The reaction between polystyrene having oxazoline groups(RPS) and chlorinated polyethylene(CPE) was investigated by FTIR, DSC methods.

用FTIR、DSC方法研究了含恶唑啉官能团的聚苯乙(RPS)化聚乙(CPE)之间的反应。

The thermal decomposition of single, double-and triple-base nitroguanidine propellants was studied by differential scanning calorimetry (DSC).

用差示扫描量热计（DSC）研究了单基、双基和三基药热分解性能。

The structure and properties of polyorganosiloxane-acrylate emulsion copolymer were investigated by IR, XPS, DSC, 1H-NMR, WAXD.

利用红外光谱、光电子能谱、差热分析、核磁共振、X射线衍射方法对聚硅氧改性丙酸酯共聚物的结构和性能进行了研究。

The dehydriding temperature and dehydriding capacity were evaluated by differential scanning calorimeter (DSC) and thermogravimetric analysis (TG).

运用差热分析和热重分析对储氢材料的放氢温度和放氢量进行了测试。

The crystallization porperty of polycaprolactam(PA6)-polyethylene glycol(PEG)block copolymer wasinvestigated by means of electron microscope,x-ray diffraction,DSC and hot stage polarized microscope.

应用DSC、热台、扫描电以及偏光显研究了PA6-PEG嵌段共聚物的结晶性能。

The effect of ethylene comonomer content on the crystallization, mechanical and viscoelastic properties of VERSIFY copolymers was studied by DSC, DMTA, POM and WAXD.

通过DSC，DMTA，POM和WAXD手段，研究了乙共聚单体含量的变化对VERSIFY共聚物结晶性能、力学性能和粘弹性能的影响。

During heating,phase transformation and expansibility of the new quartz sands and the calcined Quartz sands from two places were determined by DSC and thermodilatometry.

本研究采用DSC和热膨胀仪对两种石英砂的原砂和焙烧砂在加热过程中的相变和热膨胀进行了分析。

The changing of the structure and properties of UHMWPE fibres during super drawing were studied by means of SEM, DSC, WAXD and sound pulsimeter.

还借助扫描电子显（SEM）、热分析（DSC）、广角X射线衍射（WAXD）、声速手段研究了UHMWPE熔纺丝在超拉伸过程中结构性能的变化。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

The photographs of polarizing microscope showed the number of spherocrystal was increased and the diameter was decreased after saponification reaction which was agreed with the studies of DSC.

试样的偏光显观察结果表明，醇解后，球晶数目增加、直径减小、完善程度降低。

The reaction between polystyrene having oxazoline groups(RPS) and chlorinated polyethylene(CPE) was investigated by FTIR, DSC methods.

用FTIR、DSC等方法研究了含恶唑啉官能团的聚苯乙烯(RPS)与氯化聚乙烯(CPE)之间的反应。

The thermal decomposition of single, double-and triple-base nitroguanidine propellants was studied by differential scanning calorimetry (DSC).

用差示扫描量计（DSC）研究了单基、双基和三基药解性能。

The structure and properties of polyorganosiloxane-acrylate emulsion copolymer were investigated by IR, XPS, DSC, 1H-NMR, WAXD.

利用红外、电子能、差、核磁共振、X射线衍射等方法对聚硅氧改性丙烯酸酯共聚物的结构和性能进行了研究。

The dehydriding temperature and dehydriding capacity were evaluated by differential scanning calorimeter (DSC) and thermogravimetric analysis (TG).

运用差和重对储氢材料的放氢温度和放氢量进行了测试。

The crystallization porperty of polycaprolactam(PA6)-polyethylene glycol(PEG)block copolymer wasinvestigated by means of electron microscope,x-ray diffraction,DSC and hot stage polarized microscope.

应用DSC、台、扫描电镜以及偏显微镜等研究了PA6-PEG嵌段共聚物的结晶性能。

The effect of ethylene comonomer content on the crystallization, mechanical and viscoelastic properties of VERSIFY copolymers was studied by DSC, DMTA, POM and WAXD.

通过DSC，DMTA，POM和WAXD等手段，研究了乙烯共聚单体含量的变化对VERSIFY共聚物结晶性能、力学性能和粘弹性能的影响。

During heating,phase transformation and expansibility of the new quartz sands and the calcined Quartz sands from two places were determined by DSC and thermodilatometry.

本研究采用DSC和膨胀仪对两种石英砂的原砂和焙烧砂在加过程中的相变和膨胀进行了。

The changing of the structure and properties of UHMWPE fibres during super drawing were studied by means of SEM, DSC, WAXD and sound pulsimeter.

还借助扫描电子显微镜（SEM）、（DSC）、广角X射线衍射（WAXD）、声速等手段研究了UHMWPE熔纺丝在超拉伸过程中结构性能的变化。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外及DSC曲线，认为苯甲酸铅是一种催化型固化剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外及DSC曲线，认为苯甲酸铅是一种催化型固化剂。

The photographs of polarizing microscope showed the number of spherocrystal was increased and the diameter was decreased after saponification reaction which was agreed with the studies of DSC.

试样的偏显微镜观察结果表明，醇解后，球晶数目增加、直径减小、完善程度降低。

The reaction between polystyrene having oxazoline groups(RPS) and chlorinated polyethylene(CPE) was investigated by FTIR, DSC methods.

用FTIR、DSC等方法研究了含恶唑啉官能团的苯乙(RPS)与氯化乙(CPE)之间的反应。

The thermal decomposition of single, double-and triple-base nitroguanidine propellants was studied by differential scanning calorimetry (DSC).

用差示扫描量热计（DSC）研究了单基、双基和三基药热分解能。

The structure and properties of polyorganosiloxane-acrylate emulsion copolymer were investigated by IR, XPS, DSC, 1H-NMR, WAXD.

利用红外光谱、光电子能谱、差热分析、核磁共振、X射线衍射等方法氧改酸酯共物的结构和能进行了研究。

The dehydriding temperature and dehydriding capacity were evaluated by differential scanning calorimeter (DSC) and thermogravimetric analysis (TG).

运用差热分析和热重分析储氢材料的放氢温度和放氢量进行了测试。

The crystallization porperty of polycaprolactam(PA6)-polyethylene glycol(PEG)block copolymer wasinvestigated by means of electron microscope,x-ray diffraction,DSC and hot stage polarized microscope.

应用DSC、热台、扫描电镜以及偏光显微镜等研究了PA6-PEG嵌段共物的结晶能。

The effect of ethylene comonomer content on the crystallization, mechanical and viscoelastic properties of VERSIFY copolymers was studied by DSC, DMTA, POM and WAXD.

通过DSC，DMTA，POM和WAXD等手段，研究了乙共单体含量的变化VERSIFY共物结晶能、力学能和粘弹能的影响。

During heating,phase transformation and expansibility of the new quartz sands and the calcined Quartz sands from two places were determined by DSC and thermodilatometry.

本研究采用DSC和热膨胀仪两种石英砂的原砂和焙烧砂在加热过程中的相变和热膨胀进行了分析。

The changing of the structure and properties of UHMWPE fibres during super drawing were studied by means of SEM, DSC, WAXD and sound pulsimeter.

还借助扫描电子显微镜（SEM）、热分析（DSC）、广角X射线衍射（WAXD）、声速等手段研究了UHMWPE熔纺丝在超拉伸过程中结构能的变化。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

The photographs of polarizing microscope showed the number of spherocrystal was increased and the diameter was decreased after saponification reaction which was agreed with the studies of DSC.

试样的偏光显微镜观察结果表明，醇解后，球晶数目增加、直径减小、完善程度降低。

The reaction between polystyrene having oxazoline groups(RPS) and chlorinated polyethylene(CPE) was investigated by FTIR, DSC methods.

用FTIR、DSC等方法研究唑啉官能团的聚苯乙烯(RPS)与氯化聚乙烯(CPE)之间的反应。

The thermal decomposition of single, double-and triple-base nitroguanidine propellants was studied by differential scanning calorimetry (DSC).

用差示扫描量热计（DSC）研究单基、双基和三基药热分解能。

The structure and properties of polyorganosiloxane-acrylate emulsion copolymer were investigated by IR, XPS, DSC, 1H-NMR, WAXD.

利用红外光谱、光电子能谱、差热分析、核磁共振、X射线衍射等方法对聚硅氧改丙烯酸酯共聚物的构和能进行研究。

The dehydriding temperature and dehydriding capacity were evaluated by differential scanning calorimeter (DSC) and thermogravimetric analysis (TG).

运用差热分析和热重分析对储氢材料的放氢温度和放氢量进行测试。

The crystallization porperty of polycaprolactam(PA6)-polyethylene glycol(PEG)block copolymer wasinvestigated by means of electron microscope,x-ray diffraction,DSC and hot stage polarized microscope.

应用DSC、热台、扫描电镜以及偏光显微镜等研究PA6-PEG嵌段共聚物的能。

The effect of ethylene comonomer content on the crystallization, mechanical and viscoelastic properties of VERSIFY copolymers was studied by DSC, DMTA, POM and WAXD.

通过DSC，DMTA，POM和WAXD等手段，研究乙烯共聚单体量的变化对VERSIFY共聚物能、力学能和粘弹能的影响。

During heating,phase transformation and expansibility of the new quartz sands and the calcined Quartz sands from two places were determined by DSC and thermodilatometry.

本研究采用DSC和热膨胀仪对两种石英砂的原砂和焙烧砂在加热过程中的相变和热膨胀进行分析。

The changing of the structure and properties of UHMWPE fibres during super drawing were studied by means of SEM, DSC, WAXD and sound pulsimeter.

还借助扫描电子显微镜（SEM）、热分析（DSC）、广角X射线衍射（WAXD）、声速等手段研究UHMWPE熔纺丝在超拉伸过程中构能的变化。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

The photographs of polarizing microscope showed the number of spherocrystal was increased and the diameter was decreased after saponification reaction which was agreed with the studies of DSC.

试样的偏光显微镜观察果表明，醇解后，球数目增加、直径减小、完善程度降低。

The reaction between polystyrene having oxazoline groups(RPS) and chlorinated polyethylene(CPE) was investigated by FTIR, DSC methods.

用FTIR、DSC等方法研究了含恶唑啉官能团的苯乙烯(RPS)与乙烯(CPE)之间的反应。

The thermal decomposition of single, double-and triple-base nitroguanidine propellants was studied by differential scanning calorimetry (DSC).

用差示扫描量热计（DSC）研究了单基、双基和三基药热分解性能。

The structure and properties of polyorganosiloxane-acrylate emulsion copolymer were investigated by IR, XPS, DSC, 1H-NMR, WAXD.

利用红外谱、电子能谱、差热分析、核磁共振、X射线衍射等方法对硅氧改性丙烯酸酯共物的结构和性能进行了研究。

The dehydriding temperature and dehydriding capacity were evaluated by differential scanning calorimeter (DSC) and thermogravimetric analysis (TG).

运用差热分析和热重分析对储氢材料的放氢温度和放氢量进行了测试。

The crystallization porperty of polycaprolactam(PA6)-polyethylene glycol(PEG)block copolymer wasinvestigated by means of electron microscope,x-ray diffraction,DSC and hot stage polarized microscope.

应用DSC、热台、扫描电镜以及偏镜等研究了PA6-PEG嵌段共物的结晶性能。

The effect of ethylene comonomer content on the crystallization, mechanical and viscoelastic properties of VERSIFY copolymers was studied by DSC, DMTA, POM and WAXD.

通过DSC，DMTA，POM和WAXD等手段，研究了乙烯共单体含量的变对VERSIFY共物结晶性能、力学性能和粘弹性能的影响。

During heating,phase transformation and expansibility of the new quartz sands and the calcined Quartz sands from two places were determined by DSC and thermodilatometry.

本研究采用DSC和热膨胀仪对两种石英砂的原砂和焙烧砂在加热过程中的相变和热膨胀进行了分析。

The changing of the structure and properties of UHMWPE fibres during super drawing were studied by means of SEM, DSC, WAXD and sound pulsimeter.

还借助扫描电子镜（SEM）、热分析（DSC）、广角X射线衍射（WAXD）、声速等手段研究了UHMWPE熔纺丝在超拉伸过程中结构性能的变。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固剂，通过对环氧树脂固物的红外谱及DSC曲线分析，认为苯甲酸铅是一种催型固剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固剂，通过对环氧树脂固物的红外谱及DSC曲线分析，认为苯甲酸铅是一种催型固剂。

The photographs of polarizing microscope showed the number of spherocrystal was increased and the diameter was decreased after saponification reaction which was agreed with the studies of DSC.

试样的偏镜观察结果表明，醇解后，球晶数目增加、直径减小、完善程度降低。