The reaction between polystyrene having oxazoline groups(RPS) and chlorinated polyethylene(CPE) was investigated by FTIR, DSC methods.

用FTIR、DSC等方法研究了含恶唑啉官能团的聚苯乙烯(RPS)与氯化聚乙烯(CPE)之间的反应。

The thermal decomposition of single, double-and triple-base nitroguanidine propellants was studied by differential scanning calorimetry (DSC).

用差示扫描量热计（DSC）研究了单基、双基和三基药热能。

The structure and properties of polyorganosiloxane-acrylate emulsion copolymer were investigated by IR, XPS, DSC, 1H-NMR, WAXD.

利用红外光谱、光电子能谱、差热析、核磁共振、X射线衍射等方法聚硅氧改丙烯酸酯共聚物的结构和能进行了研究。

The dehydriding temperature and dehydriding capacity were evaluated by differential scanning calorimeter (DSC) and thermogravimetric analysis (TG).

运用差热析和热重析材料的放温度和放量进行了测试。

The crystallization porperty of polycaprolactam(PA6)-polyethylene glycol(PEG)block copolymer wasinvestigated by means of electron microscope,x-ray diffraction,DSC and hot stage polarized microscope.

应用DSC、热台、扫描电镜以及偏光显微镜等研究了PA6-PEG嵌段共聚物的结晶能。

The effect of ethylene comonomer content on the crystallization, mechanical and viscoelastic properties of VERSIFY copolymers was studied by DSC, DMTA, POM and WAXD.

通过DSC，DMTA，POM和WAXD等手段，研究了乙烯共聚单体含量的变化VERSIFY共聚物结晶能、力学能和粘弹能的影响。

During heating,phase transformation and expansibility of the new quartz sands and the calcined Quartz sands from two places were determined by DSC and thermodilatometry.

本研究采用DSC和热膨胀仪两种石英砂的原砂和焙烧砂在加热过程中的相变和热膨胀进行了析。

The changing of the structure and properties of UHMWPE fibres during super drawing were studied by means of SEM, DSC, WAXD and sound pulsimeter.

还借助扫描电子显微镜（SEM）、热析（DSC）、广角X射线衍射（WAXD）、声速等手段研究了UHMWPE熔纺丝在超拉伸过程中结构能的变化。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过环氧树脂固化物的红外光谱及DSC曲线析，认为苯甲酸铅是一种催化型固化剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过环氧树脂固化物的红外光谱及DSC曲线析，认为苯甲酸铅是一种催化型固化剂。

The photographs of polarizing microscope showed the number of spherocrystal was increased and the diameter was decreased after saponification reaction which was agreed with the studies of DSC.

试样的偏光显微镜观察结果表明，醇后，球晶数目增加、直径减小、完善程度降低。

The reaction between polystyrene having oxazoline groups(RPS) and chlorinated polyethylene(CPE) was investigated by FTIR, DSC methods.

用FTIR、DSC等方法研究含恶唑啉官能团的聚苯乙烯(RPS)与氯化聚乙烯(CPE)之间的反应。

The thermal decomposition of single, double-and triple-base nitroguanidine propellants was studied by differential scanning calorimetry (DSC).

用差示扫描量计（DSC）研究单基、双基和三基药解性能。

The structure and properties of polyorganosiloxane-acrylate emulsion copolymer were investigated by IR, XPS, DSC, 1H-NMR, WAXD.

利用红外光谱、光电子能谱、差、核磁共振、X射线衍射等方法对聚硅氧改性丙烯酸酯共聚物的结构和性能研究。

The dehydriding temperature and dehydriding capacity were evaluated by differential scanning calorimeter (DSC) and thermogravimetric analysis (TG).

运用差和重对储氢材料的放氢温度和放氢量测试。

The crystallization porperty of polycaprolactam(PA6)-polyethylene glycol(PEG)block copolymer wasinvestigated by means of electron microscope,x-ray diffraction,DSC and hot stage polarized microscope.

应用DSC、台、扫描电镜以及偏光显微镜等研究PA6-PEG嵌段共聚物的结晶性能。

The effect of ethylene comonomer content on the crystallization, mechanical and viscoelastic properties of VERSIFY copolymers was studied by DSC, DMTA, POM and WAXD.

通过DSC，DMTA，POM和WAXD等手段，研究乙烯共聚单体含量的变化对VERSIFY共聚物结晶性能、力学性能和粘弹性能的影响。

During heating,phase transformation and expansibility of the new quartz sands and the calcined Quartz sands from two places were determined by DSC and thermodilatometry.

本研究采用DSC和膨胀仪对两种石英砂的原砂和焙烧砂在加过程中的相变和膨胀。

The changing of the structure and properties of UHMWPE fibres during super drawing were studied by means of SEM, DSC, WAXD and sound pulsimeter.

还借助扫描电子显微镜（SEM）、（DSC）、广角X射线衍射（WAXD）、声速等手段研究UHMWPE熔纺丝在超拉伸过程中结构性能的变化。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线，认为苯甲酸铅是一种催化型固化剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线，认为苯甲酸铅是一种催化型固化剂。

The photographs of polarizing microscope showed the number of spherocrystal was increased and the diameter was decreased after saponification reaction which was agreed with the studies of DSC.

试样的偏光显微镜观察结果表明，醇解后，球晶数目增加、直径减小、完善程度降低。

The reaction between polystyrene having oxazoline groups(RPS) and chlorinated polyethylene(CPE) was investigated by FTIR, DSC methods.

用FTIR、DSC等方法研究了含恶唑啉官能团的聚苯乙烯(RPS)与氯聚乙烯(CPE)之间的反应。

The thermal decomposition of single, double-and triple-base nitroguanidine propellants was studied by differential scanning calorimetry (DSC).

用差示扫描量热计（DSC）研究了单基、双基和三基药热分解性能。

The structure and properties of polyorganosiloxane-acrylate emulsion copolymer were investigated by IR, XPS, DSC, 1H-NMR, WAXD.

利用红外光谱、光电子能谱、差热分析、核磁共振、X射线衍射等方法聚硅氧改性丙烯酸酯共聚物的结构和性能进行了研究。

The dehydriding temperature and dehydriding capacity were evaluated by differential scanning calorimeter (DSC) and thermogravimetric analysis (TG).

运用差热分析和热重分析储氢材料的放氢温度和放氢量进行了测试。

The crystallization porperty of polycaprolactam(PA6)-polyethylene glycol(PEG)block copolymer wasinvestigated by means of electron microscope,x-ray diffraction,DSC and hot stage polarized microscope.

应用DSC、热台、扫描电镜以及偏光显微镜等研究了PA6-PEG嵌段共聚物的结晶性能。

The effect of ethylene comonomer content on the crystallization, mechanical and viscoelastic properties of VERSIFY copolymers was studied by DSC, DMTA, POM and WAXD.

通过DSC，DMTA，POM和WAXD等手段，研究了乙烯共聚单体含量的VERSIFY共聚物结晶性能、力学性能和粘弹性能的影响。

During heating,phase transformation and expansibility of the new quartz sands and the calcined Quartz sands from two places were determined by DSC and thermodilatometry.

本研究采用DSC和热膨胀仪两种石英砂的原砂和焙烧砂在加热过程中的相和热膨胀进行了分析。

The changing of the structure and properties of UHMWPE fibres during super drawing were studied by means of SEM, DSC, WAXD and sound pulsimeter.

还借助扫描电子显微镜（SEM）、热分析（DSC）、广角X射线衍射（WAXD）、声速等手段研究了UHMWPE熔纺丝在超拉伸过程中结构性能的。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固剂，通过环氧树脂固物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催型固剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固剂，通过环氧树脂固物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催型固剂。

The photographs of polarizing microscope showed the number of spherocrystal was increased and the diameter was decreased after saponification reaction which was agreed with the studies of DSC.

试样的偏光显微镜观察结果表明，醇解后，球晶数目增加、直径减小、完善程度降低。

The reaction between polystyrene having oxazoline groups(RPS) and chlorinated polyethylene(CPE) was investigated by FTIR, DSC methods.

用FTIR、DSC等方法了含恶唑啉官团的聚苯乙烯(RPS)与氯化聚乙烯(CPE)之间的反应。

The thermal decomposition of single, double-and triple-base nitroguanidine propellants was studied by differential scanning calorimetry (DSC).

用差示扫描量热计（DSC）了单基、双基和三基药热分解性。

The structure and properties of polyorganosiloxane-acrylate emulsion copolymer were investigated by IR, XPS, DSC, 1H-NMR, WAXD.

利用红外光谱、光电子谱、差热分析、核磁共振、X射线衍射等方法对聚硅氧改性丙烯酸酯共聚物的结构和性进行了。

The dehydriding temperature and dehydriding capacity were evaluated by differential scanning calorimeter (DSC) and thermogravimetric analysis (TG).

运用差热分析和热重分析对储氢材料的放氢温度和放氢量进行了测试。

The crystallization porperty of polycaprolactam(PA6)-polyethylene glycol(PEG)block copolymer wasinvestigated by means of electron microscope,x-ray diffraction,DSC and hot stage polarized microscope.

应用DSC、热台、扫描电镜以及偏光显微镜等了PA6-PEG嵌段共聚物的结晶性。

The effect of ethylene comonomer content on the crystallization, mechanical and viscoelastic properties of VERSIFY copolymers was studied by DSC, DMTA, POM and WAXD.

DSC，DMTA，POM和WAXD等手段，了乙烯共聚单体含量的变化对VERSIFY共聚物结晶性、力学性和粘弹性的影响。

During heating,phase transformation and expansibility of the new quartz sands and the calcined Quartz sands from two places were determined by DSC and thermodilatometry.

本采用DSC和热膨胀仪对两种石英砂的原砂和焙烧砂在加热程中的相变和热膨胀进行了分析。

The changing of the structure and properties of UHMWPE fibres during super drawing were studied by means of SEM, DSC, WAXD and sound pulsimeter.

还借助扫描电子显微镜（SEM）、热分析（DSC）、广角X射线衍射（WAXD）、声速等手段了UHMWPE熔纺丝在超拉伸程中结构性的变化。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

The photographs of polarizing microscope showed the number of spherocrystal was increased and the diameter was decreased after saponification reaction which was agreed with the studies of DSC.

试样的偏光显微镜观察结果表明，醇解后，球晶数目增加、直径减小、完善程度降低。

The reaction between polystyrene having oxazoline groups(RPS) and chlorinated polyethylene(CPE) was investigated by FTIR, DSC methods.

用FTIR、DSC等方法研究了含恶唑啉官能团的苯乙烯(RPS)与氯化乙烯(CPE)之间的反应。

The thermal decomposition of single, double-and triple-base nitroguanidine propellants was studied by differential scanning calorimetry (DSC).

用差示扫描量热计（DSC）研究了单基、双基和三基药热分解性能。

The structure and properties of polyorganosiloxane-acrylate emulsion copolymer were investigated by IR, XPS, DSC, 1H-NMR, WAXD.

利用红外光谱、光电子能谱、差热分析、核磁振、X射线衍射等方法对硅氧改性丙烯酸酯的结构和性能进行了研究。

The dehydriding temperature and dehydriding capacity were evaluated by differential scanning calorimeter (DSC) and thermogravimetric analysis (TG).

运用差热分析和热重分析对储氢材料的放氢温度和放氢量进行了测试。

The crystallization porperty of polycaprolactam(PA6)-polyethylene glycol(PEG)block copolymer wasinvestigated by means of electron microscope,x-ray diffraction,DSC and hot stage polarized microscope.

应用DSC、热台、扫描电镜以及偏光显微镜等研究了PA6-PEG嵌段的结晶性能。

The effect of ethylene comonomer content on the crystallization, mechanical and viscoelastic properties of VERSIFY copolymers was studied by DSC, DMTA, POM and WAXD.

通过DSC，DMTA，POM和WAXD等手段，研究了乙烯单体含量的变化对VERSIFY结晶性能、力学性能和粘弹性能的影响。

During heating,phase transformation and expansibility of the new quartz sands and the calcined Quartz sands from two places were determined by DSC and thermodilatometry.

本研究采用DSC和热膨胀仪对两种石英砂的原砂和焙烧砂在加热过程中的相变和热膨胀进行了分析。

The changing of the structure and properties of UHMWPE fibres during super drawing were studied by means of SEM, DSC, WAXD and sound pulsimeter.

还借助扫描电子显微镜（SEM）、热分析（DSC）、广角X射线衍射（WAXD）、声速等手段研究了UHMWPE熔纺丝在超拉伸过程中结构性能的变化。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过对环氧树脂固化的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过对环氧树脂固化的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

The photographs of polarizing microscope showed the number of spherocrystal was increased and the diameter was decreased after saponification reaction which was agreed with the studies of DSC.

试样的偏光显微镜观察结果表明，醇解后，球晶数目增加、直径减小、完善程度降低。

The reaction between polystyrene having oxazoline groups(RPS) and chlorinated polyethylene(CPE) was investigated by FTIR, DSC methods.

用FTIR、DSC等方法研究了含恶唑啉官能团的聚苯乙烯(RPS)与氯化聚乙烯(CPE)之间的反应。

The thermal decomposition of single, double-and triple-base nitroguanidine propellants was studied by differential scanning calorimetry (DSC).

用差示扫描量热计（DSC）研究了单基、双基和三基药热分解能。

The structure and properties of polyorganosiloxane-acrylate emulsion copolymer were investigated by IR, XPS, DSC, 1H-NMR, WAXD.

利用红外光谱、光电子能谱、差热分析、核磁共振、X射线衍射等方法对聚丙烯酸酯共聚物的结构和能进行了研究。

The dehydriding temperature and dehydriding capacity were evaluated by differential scanning calorimeter (DSC) and thermogravimetric analysis (TG).

运用差热分析和热重分析对储氢材料的放氢温度和放氢量进行了测试。

The crystallization porperty of polycaprolactam(PA6)-polyethylene glycol(PEG)block copolymer wasinvestigated by means of electron microscope,x-ray diffraction,DSC and hot stage polarized microscope.

应用DSC、热台、扫描电镜以及偏光显微镜等研究了PA6-PEG嵌段共聚物的结晶能。

The effect of ethylene comonomer content on the crystallization, mechanical and viscoelastic properties of VERSIFY copolymers was studied by DSC, DMTA, POM and WAXD.

通过DSC，DMTA，POM和WAXD等手段，研究了乙烯共聚单体含量的变化对VERSIFY共聚物结晶能、力学能和粘弹能的影响。

During heating,phase transformation and expansibility of the new quartz sands and the calcined Quartz sands from two places were determined by DSC and thermodilatometry.

本研究采用DSC和热膨胀仪对两种石英砂的原砂和焙烧砂在加热过程中的相变和热膨胀进行了分析。

The changing of the structure and properties of UHMWPE fibres during super drawing were studied by means of SEM, DSC, WAXD and sound pulsimeter.

还借助扫描电子显微镜（SEM）、热分析（DSC）、广角X射线衍射（WAXD）、声速等手段研究了UHMWPE熔纺丝在超拉伸过程中结构能的变化。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过对环树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过对环树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

The photographs of polarizing microscope showed the number of spherocrystal was increased and the diameter was decreased after saponification reaction which was agreed with the studies of DSC.

试样的偏光显微镜观察结果表明，醇解后，球晶数目增加、直径减小、完善程度降低。

The reaction between polystyrene having oxazoline groups(RPS) and chlorinated polyethylene(CPE) was investigated by FTIR, DSC methods.

用FTIR、DSC等方法研究含恶唑啉官能团的聚苯(RPS)与氯化聚(CPE)之间的反应。

The thermal decomposition of single, double-and triple-base nitroguanidine propellants was studied by differential scanning calorimetry (DSC).

用差示扫描量热计（DSC）研究单基、双基和三基药热分解性能。

The structure and properties of polyorganosiloxane-acrylate emulsion copolymer were investigated by IR, XPS, DSC, 1H-NMR, WAXD.

利用红外光谱、光电子能谱、差热分析、核磁共振、X射线衍射等方法对聚硅氧改性丙酸酯共聚物的结构和性能进行研究。

The dehydriding temperature and dehydriding capacity were evaluated by differential scanning calorimeter (DSC) and thermogravimetric analysis (TG).

运用差热分析和热重分析对储氢材料的放氢温度和放氢量进行测试。

The crystallization porperty of polycaprolactam(PA6)-polyethylene glycol(PEG)block copolymer wasinvestigated by means of electron microscope,x-ray diffraction,DSC and hot stage polarized microscope.

应用DSC、热台、扫描电镜以及偏光显微镜等研究PA6-PEG嵌段共聚物的结晶性能。

The effect of ethylene comonomer content on the crystallization, mechanical and viscoelastic properties of VERSIFY copolymers was studied by DSC, DMTA, POM and WAXD.

通过DSC，DMTA，POM和WAXD等手段，研究共聚单体含量的变化对VERSIFY共聚物结晶性能、力学性能和粘弹性能的影响。

During heating,phase transformation and expansibility of the new quartz sands and the calcined Quartz sands from two places were determined by DSC and thermodilatometry.

本研究采用DSC和热膨胀仪对两种石英砂的原砂和焙烧砂在加热过程中的相变和热膨胀进行分析。

The changing of the structure and properties of UHMWPE fibres during super drawing were studied by means of SEM, DSC, WAXD and sound pulsimeter.

还借助扫描电子显微镜（SEM）、热分析（DSC）、广角X射线衍射（WAXD）、声速等手段研究UHMWPE熔纺丝在超拉伸过程中结构性能的变化。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

The photographs of polarizing microscope showed the number of spherocrystal was increased and the diameter was decreased after saponification reaction which was agreed with the studies of DSC.

试样的偏光显微镜观察结果表明，醇解后，球晶数目增加、直径减小、完善程度降低。

The reaction between polystyrene having oxazoline groups(RPS) and chlorinated polyethylene(CPE) was investigated by FTIR, DSC methods.

用FTIR、DSC法研究了含恶唑啉官能团的聚苯乙烯(RPS)与氯化聚乙烯(CPE)之间的反应。

The thermal decomposition of single, double-and triple-base nitroguanidine propellants was studied by differential scanning calorimetry (DSC).

用差示扫描量热计（DSC）研究了单基、双基和三基药热分解性能。

The structure and properties of polyorganosiloxane-acrylate emulsion copolymer were investigated by IR, XPS, DSC, 1H-NMR, WAXD.

利用红外光谱、光电子能谱、差热分析、核磁振、X射线衍射法对聚硅氧改性丙烯聚物的结构和性能进行了研究。

The dehydriding temperature and dehydriding capacity were evaluated by differential scanning calorimeter (DSC) and thermogravimetric analysis (TG).

运用差热分析和热重分析对储氢材料的放氢温度和放氢量进行了测试。

The crystallization porperty of polycaprolactam(PA6)-polyethylene glycol(PEG)block copolymer wasinvestigated by means of electron microscope,x-ray diffraction,DSC and hot stage polarized microscope.

应用DSC、热台、扫描电镜以及偏光显微镜研究了PA6-PEG嵌段聚物的结晶性能。

The effect of ethylene comonomer content on the crystallization, mechanical and viscoelastic properties of VERSIFY copolymers was studied by DSC, DMTA, POM and WAXD.

通过DSC，DMTA，POM和WAXD手段，研究了乙烯聚单体含量的变化对VERSIFY聚物结晶性能、力学性能和粘弹性能的影响。

During heating,phase transformation and expansibility of the new quartz sands and the calcined Quartz sands from two places were determined by DSC and thermodilatometry.

本研究采用DSC和热膨胀仪对两种石英砂的原砂和焙烧砂在加热过程中的相变和热膨胀进行了分析。

The changing of the structure and properties of UHMWPE fibres during super drawing were studied by means of SEM, DSC, WAXD and sound pulsimeter.

还借助扫描电子显微镜（SEM）、热分析（DSC）、广角X射线衍射（WAXD）、声速手段研究了UHMWPE熔纺丝在超拉伸过程中结构性能的变化。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲铅是一种催化型固化剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲铅是一种催化型固化剂。

The photographs of polarizing microscope showed the number of spherocrystal was increased and the diameter was decreased after saponification reaction which was agreed with the studies of DSC.

试样的偏光显微镜观察结果表明，醇解后，球晶数目增加、直径减小、完善程度降低。

The reaction between polystyrene having oxazoline groups(RPS) and chlorinated polyethylene(CPE) was investigated by FTIR, DSC methods.

FTIR、DSC等方法研了含恶唑啉官团的聚苯乙烯(RPS)与氯化聚乙烯(CPE)之间的反应。

The thermal decomposition of single, double-and triple-base nitroguanidine propellants was studied by differential scanning calorimetry (DSC).

差示扫描量热计（DSC）研了单基、双基和三基药热分解性。

The structure and properties of polyorganosiloxane-acrylate emulsion copolymer were investigated by IR, XPS, DSC, 1H-NMR, WAXD.

利红外光、光电、差热分析、核磁共振、X射线衍射等方法对聚硅氧改性丙烯酸酯共聚物的结构和性进行了研。

The dehydriding temperature and dehydriding capacity were evaluated by differential scanning calorimeter (DSC) and thermogravimetric analysis (TG).

差热分析和热重分析对储氢材料的放氢温度和放氢量进行了测试。

The crystallization porperty of polycaprolactam(PA6)-polyethylene glycol(PEG)block copolymer wasinvestigated by means of electron microscope,x-ray diffraction,DSC and hot stage polarized microscope.

应DSC、热台、扫描电镜以及偏光显微镜等研了PA6-PEG嵌段共聚物的结晶性。

The effect of ethylene comonomer content on the crystallization, mechanical and viscoelastic properties of VERSIFY copolymers was studied by DSC, DMTA, POM and WAXD.

通过DSC，DMTA，POM和WAXD等手段，研了乙烯共聚单体含量的变化对VERSIFY共聚物结晶性、力学性和粘弹性的影响。

During heating,phase transformation and expansibility of the new quartz sands and the calcined Quartz sands from two places were determined by DSC and thermodilatometry.

本研采DSC和热膨胀仪对两种石英砂的原砂和焙烧砂在加热过程中的相变和热膨胀进行了分析。

The changing of the structure and properties of UHMWPE fibres during super drawing were studied by means of SEM, DSC, WAXD and sound pulsimeter.

还借助扫描电显微镜（SEM）、热分析（DSC）、广角X射线衍射（WAXD）、声速等手段研了UHMWPE熔纺丝在超拉伸过程中结构性的变化。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

The photographs of polarizing microscope showed the number of spherocrystal was increased and the diameter was decreased after saponification reaction which was agreed with the studies of DSC.

试样的偏光显微镜观察结果表明，醇解后，球晶数目增加、直径减小、完善程度降低。