The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.

利用光学显微、扫、能谱分析等试验手段对铝箔中"桔瓣"形针孔形成的原因进行了分析。

SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.

借助扫观察到细化的叶片表面的钴微粒形核核心,通过能谱分析手段,究型壳内表层的白色物质的相组成。

The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.

摘要针对日照厂2(上标﹟)锅炉屏式过热器泄漏进行了金相试验、晶间腐蚀倾向性试验和能谱分析。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形分析、光学金相、扫能谱分析等测试方法，究了双层药皮对钛钙型不锈钢焊条气孔的影响。

The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.

利用光学显微镜、扫描电镜、能谱析等试验手段对铝箔中"桔瓣"形针孔形成的原因析。

SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.

借助扫描电镜观察到细化的叶片表面的钴微粒形核核心,通过能谱析手段,究型壳内表层的白色物质的相组成。

The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.

摘要针对日照电厂2(上标﹟)锅炉屏式过热器泄金相试验、晶间腐蚀倾向性试验和电镜能谱析。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形析、光学金相、扫描电镜能谱析等测试方法，究双层药皮对钛钙型不锈钢焊条气孔的影响。

The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.

利用光学显微镜、扫描电镜、能谱析等试验手段对铝箔中"桔瓣"形针孔形成的原因析。

SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.

借助扫描电镜观察到细化的叶片表面的钴微粒形核核心,通过能谱析手段,究型壳内表层的白色物质的相组成。

The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.

摘要针对日照电厂2(上标﹟)锅炉屏式过热器泄金相试验、晶间腐蚀倾向性试验和电镜能谱析。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形析、光学金相、扫描电镜能谱析等测试方法，究双层药皮对钛钙型不锈钢焊条气孔的影响。

The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.

利用光学显微镜、扫描电镜、能谱分析等试验手段对铝箔中"桔瓣"形针孔形成的原因分析。

SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.

借助扫描电镜观察到细化的叶片表面的钴微粒形核核心,通过能谱分析手段,究型壳内表层的白色物质的相组成。

The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.

摘要针对日照电厂2(上标﹟)锅炉屏式过热器泄漏金相试验、晶间腐蚀倾向性试验和电镜能谱分析。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形分析、光学金相、扫描电镜能谱分析等测试方法，究双层药皮对钛钙型不锈钢焊条气孔的影响。

The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.

利用光学显微镜、扫描电镜、能谱分析等试验手段对铝箔""形针孔形成的原因进行了分析。

SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.

借助扫描电镜观察到细化的叶片表面的钴微粒形核核心,通过能谱分析手段,究型壳内表层的白色物质的相组成。

The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.

摘要针对日照电厂2(上标﹟)锅炉屏式过热器泄漏进行了金相试验、晶间腐蚀试验和电镜能谱分析。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形分析、光学金相、扫描电镜能谱分析等测试方法，究了双层药皮对钛钙型不锈钢焊条气孔的影响。

The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.

利用光学显微镜、扫描电镜、析手段对铝箔中"桔瓣"形针孔形成的原因进行了析。

SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.

借助扫描电镜观察到细化的叶片表面的钴微粒形核核心,通过析手段,究型壳内表层的白色物质的相组成。

The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.

摘要针对日照电厂2(上标﹟)锅炉屏式过热器泄漏进行了金相、晶间腐蚀倾向性和电镜析。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形析、光学金相、扫描电镜析测方法，究了双层药皮对钛钙型不锈钢焊条气孔的影响。

The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.

利用光学显微镜、扫描电镜、能谱分析等试验手段对铝箔中"桔瓣"形针孔形成的原因进行了分析。

SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.

借助扫描电镜观化的叶片表面的钴微粒形核核心,通过能谱分析手段,究型壳内表层的白色物质的相组成。

The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.

摘要针对日照电2(﹟)锅炉屏式过热器泄漏进行了金相试验、晶间腐蚀倾向性试验和电镜能谱分析。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形分析、光学金相、扫描电镜能谱分析等测试方法，究了双层药皮对钛钙型不锈钢焊条气孔的影响。

The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.

利用光学显微镜、扫描电镜、能谱分析等试验手段对铝箔""形针孔形成的原因进行了分析。

SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.

借助扫描电镜观察到细化的叶片表面的钴微粒形核核心,通过能谱分析手段,究型壳内表层的白色物质的相组成。

The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.

摘要针对日照电厂2(上标﹟)锅炉屏式过热器泄漏进行了金相试验、晶间腐蚀试验和电镜能谱分析。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平板堆焊、高速摄影、波形分析、光学金相、扫描电镜能谱分析等测试方法，究了双层药皮对钛钙型不锈钢焊条气孔的影响。

The formation mechanism of orange valvule-like pinhole in rolled aluminium foil was investigated by using optical microscopy,scanning electron microscopy,and energy dispersion X-ray spectrum.

利用光学显微、扫、能谱分析等试验手段对铝箔中"桔瓣"形针孔形成的原因进行了分析。

SEM was used to observe nucleation site of Co particles, and energy spectrum analysed phase composition of white matter in endosexine of mold.

借助扫观察到细化的叶片表面的钴微粒形核核心,通过能谱分析手段,究型壳内表层的白色物质的相组成。

The tube leakage of partition overheater of No. 2 boiler in a power plant was studied by means of metallography, intergranular corrosion test and EDS.

摘要针对日照厂2(上标﹟)锅炉屏式过热器泄漏进行了金相试验、晶间腐蚀倾向性试验和能谱分析。

The effects of double coating on the pores of lime titania type stainless steel electrode are studied with high speed cinecamera, oscillograph, optical microscope, SEM with EDS, etc.

采用平、高速摄影、波形分析、光学金相、扫能谱分析等测试方法，究了双层药皮对钛钙型不锈钢条气孔的影响。